3M™ SCOTCHCAST™ ELECTRICAL INSULATING AND SEALING COMPOUND 2104C, 14.82 OZ, 10 /CASE

3MT7100029214 MFG #: 7100029214
$91.47 / EA
3M 2104C ELECTRICAL INSULATING & SEALING
  • Color: Green
  • Composition: Part A: 35 to 50% Phthalic Acid, Di-C11-14-Branched Alkyl, Esters, C13-Rich, 15 to 35% Polymethylene Polyphenylene Isocyanate, Part B: 55 to 75% Polypropylene Glycol Glycerol Triether, 5 to 20% n, n-Di 2-HydroxypropylAniLine
  • Container Size: 14.82 oz
  • Container Type: Size C/2-Part Pouch
  • Curing Time: 1 hr at 70 deg F, 20 hr at 20 deg F
  • Flash Point: 230 deg F Part A, >=230 deg F Part B
  • Form: Liquid
  • Odor/Scent: Isocyanate
  • Series: 2104
  • Specific Gravity: Part A: 1.04/Part B: 1
  • Temperature Rating: 0 to 130 deg C
3M™ Scotchcast™ electrical insulating and sealing compound 2104 has a low gel point rating to ensure curing at room temperature. The high tensile strength of the resin exhibits a semi-flexible property and good adhesion property after curing. It is ideal for electrical applications that need good handling and performance characteristics. High dielectric strength offers a very good electrical insulating property to the resin. The resin allows you to insulate conductors of multi-core splices operating at 1 kV or less. It is used in 72 N, 85 series kits. ASTM approved and rohs 2011/65/EU Compliant.
QTY
Add to List
  • Application
  • Item Features
  • Standards
For permanent splice protection applications
  • Polyurethane material
  • Container bag size c
  • Class B temperature range
  • Gel time 18 min at 73 deg f
  • 70 shore a hardness
  • 1000 vac or less voltage rating
  • 98% elongation
  • 444 psi tensile strength
  • 72-N, 85 series used in these kits
  • 0.28% moisture absorption, 1:1 mixing ratio, pale yellow part A, black part B
  • 524 V/mil dielectric strength
  • Bonds to all modern cable jackets, bonds to itself
  • Available in two part closed mixing pouch for easy mixing and pouring
  • Tough, semi-flexible, excellent multi-purpose moisture sealing resin
  • Room temperature cure, low viscosity
  • Part a -35 to 50% phthalic acid, Di-C11-14-branched alkyl, esters, C13-Rich, 15 to 35% polyethylene polyphenylene isocyanate, 15 to 25 % 1,3-butadiene, homopolymer, hydroxyterminated, 5 -20 P,P-methylenebis(phenyl isocyanate), 0 to 10% 1,1-methylenebis(isocyanatobenzene), 0 to 0.5% phenyl isocyanate, part B-55 to 75% polypropylene glycol glycerol triether, 5 to 20% N,N-Di(2-hydroxypropyl) aniline, 5 to 20% phthalic acid, Di-C11-14-branched alkyl esters, C13-rich, 1 to 10 dipropylene glycol
  • 2 years shelf life
  • Has 18 min gel time at 73 deg f (23 deg C)
  • Useful for replacing or repairing the jacket on both single- and multi-core power cables
RoHS Compliant|ASTM Approved